JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 44

coating

Fig.3: QUVA delta E 1000-hour accelerated weathering test results Fig.4: Florida 12-month natural exposure delta E test results Fig.5: Florida 12-month natural exposure delta b* test results, which measure the degree of yellowing

1000-hour QUV exposure delta E test results
Accelerated QUV testing was carried out in advance of the longer term Florida testing. Good performance under accelerated UV weathering conditions is an indicator of good long-term natural weather performance. The graph (Figure 3) shows the delta E colour change results of the four gelcoat technologies tested after 1000 hours of accelerated UV exposure. The delta E value is 3.20 for Crystic Permabright compared with 4.03 for the best-in-class Iso/NPG.

base resin (Figures 4 and 5). All four sets of gelcoat plaques were tested at the same time and subjected to 12 months of continuous exposure in Florida. Both delta E and delta b* (db*) colour change measurements were taken. The Florida colour change test results showed the colour stability performance of the gelcoat to be even better than the accelerated QUV indications. The 12-month Florida natural weathering test results for Crystic Permabright measured a delta E of 1.25 and a delta b of only 1.06. By comparison, the best-in-class marineapproved Iso/NPG had a delta E of 2.25 and a delta b* of 2.20. These colour change results are highly significant as the smallest colour difference that humans can detect with the naked eye is a delta E of 1.0. So, the exceptionally small colour change in the Crystic Permabright test plaque is virtually impossible for most people to detect. Additionally, the delta b* test results confirmed that the new advanced polymer gelcoat base with its deconjugated Iso/NPG polyester backbone, when used with the right pigment and UV additives, could significantly reduce yellowing in a white or cream gelcoat. This was a key project deliverable for the luxury yacht market, who is keen to use a gelcoat which would help maintain the showroom look and condition of a vessel for longer. The Florida test results clearly show that the new gelcoat is able to do this, providing two times better colour stability than the next best-in-class Iso/NPG and four times better than a standard isophthalic gelcoat. This dramatic improvement in gelcoat colour stability is a step change in technology for the industry.

44

Outstanding Florida 12-month UV exposure results
Scott Bader has independently tested Crystic gelcoats in Florida for a great many years. They have concluded that Florida weathering is the most accurate way of predicting how a gelcoat will resist harsh UV light over a prolonged period of time and so it is a key test for a Crystic gelcoat product to pass. This is because the extreme natural exposure conditions in Florida accelerate product weathering by an order of two to three times faster than most other locations. Once again, comparative tests were carried out between the standard Iso, the best-in-class Iso and the best-in-class Iso/NPG versus Crystic Permabright gelcoat with its new formulation and D-Iso/NPG

jec composites magazine / No67 August - September 2011

Osmotic blister performance
Alongside weather resistance, excellent



JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011

Table of Contents for the Digital Edition of JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011

Cover
Edito
Point of view: "I have a very positive view of the market" by Thomas Hedger
Contents
Agenda of Events
COMPANY & BUSINESS
- In Brief
- Automotive
APPLICATIONS
- Aeronautics
- Building & construction
- Sustainability
MARKET
- Composites
- Asia-Pacific
- Resin
-Productivity
-Human Resources
FEATURE MARINE
- Natural Fibre
- Environment
- Race boat
- Simulation
- Coating
- Bonding
RESEARCH & DEVELOPMENT
- Simulation
- Natural Fibre
TECHNOLOGY & INNOVATIONS
- RTM-S
-Software
- SMC
Index
In the world
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - Cover
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 2
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - Edito
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - Point of view: "I have a very positive view of the market" by Thomas Hedger
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 5
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - Contents
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 7
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 8
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - Agenda of Events
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - PubJEC
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - PubESI
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - - In Brief
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - - Automotive
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - - Aeronautics
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 13
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - - Building & construction
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 15
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 16
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 17
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - - Sustainability
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - - Composites
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 20
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 21
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - - Asia-Pacific
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 23
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 24
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - - Resin
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 26
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 27
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - -Productivity
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 29
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 30
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - -Human Resources
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 32
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - - Natural Fibre
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 34
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - - Environment
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 36
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 37
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - - Race boat
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 39
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - - Simulation
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 41
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - - Coating
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 43
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 44
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 45
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 46
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - - Bonding
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 48
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - - Simulation
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 50
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 51
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 52
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - - Natural Fibre
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 54
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 55
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - - RTM-S
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 57
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 58
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 59
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - -Software
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 61
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 62
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 63
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - - SMC
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - Index
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - In the world
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 67
JEC COMPOSITES MAGAZINE - Issue #67 - August/September 2011 - 68
https://www.nxtbook.fr/newpress/jeccomposites/jcm2109_142
https://www.nxtbook.fr/newpress/jeccomposites/jcm2107_141
https://www.nxtbook.fr/newpress/jeccomposites/jcm2105_140
https://www.nxtbook.fr/newpress/jeccomposites/jcm2103_139
https://www.nxtbook.fr/newpress/jeccomposites/jcm-experts-digest-additive-manufacturing-2020
https://www.nxtbook.fr/newpress/jeccomposites/jcm2101_138
https://www.nxtbook.fr/newpress/jeccomposites/jcm2011_Special_Issue4
https://www.nxtbook.fr/newpress/jeccomposites/jcm2011_137
https://www.nxtbook.fr/newpress/jeccomposites/jcm2009_136
https://www.nxtbook.fr/newpress/jeccomposites/jcm2007_135
https://www.nxtbook.fr/newpress/jeccomposites/jcm_2020_Q1_Innovation_Report
https://www.nxtbook.fr/newpress/jeccomposites/jcm2005_Special_Issue3
https://www.nxtbook.fr/newpress/jeccomposites/jcm2005_134
https://www.nxtbook.fr/newpress/jeccomposites/jcm2003_133
https://www.nxtbook.fr/newpress/jeccomposites/jcm2001_132
https://www.nxtbook.fr/newpress/jeccomposites/jcm1911_Special_Issue2
https://www.nxtbook.fr/newpress/jeccomposites/jcm1911_131
https://www.nxtbook.fr/newpress/jeccomposites/jcm1909_130
https://www.nxtbook.fr/newpress/jeccomposites/jcm1907_129
https://www.nxtbook.fr/newpress/jeccomposites/jcm1905_128
https://www.nxtbook.fr/newpress/jeccomposites/jcm1903_Special_Issue1
https://www.nxtbook.fr/newpress/jeccomposites/jcm1903_127
https://www.nxtbook.fr/newpress/jeccomposites/jcm1901_126
https://www.nxtbook.fr/newpress/jeccomposites/jcm1811_125
https://www.nxtbook.fr/newpress/jeccomposites/jcm1810_124
https://www.nxtbook.fr/newpress/jeccomposites/jcm1808_123
https://www.nxtbook.fr/newpress/jeccomposites/jcm1807_122
https://www.nxtbook.fr/newpress/jeccomposites/jcm1805_121
https://www.nxtbook.fr/newpress/jeccomposites/jcm1804_120
https://www.nxtbook.fr/newpress/jeccomposites/jcm1803_119
https://www.nxtbook.fr/newpress/jeccomposites/jcm1802_119-Supplement_Innovation_Report
https://www.nxtbook.fr/newpress/jeccomposites/jcm1801_118
https://www.nxtbook.fr/newpress/jeccomposites/jcm1711_117
https://www.nxtbook.fr/newpress/jeccomposites/jcm1710_116
https://www.nxtbook.fr/newpress/jeccomposites/jcm1708_115
https://www.nxtbook.fr/newpress/jeccomposites/jcm1707_114
https://www.nxtbook.fr/newpress/jeccomposites/jcm1706_113
https://www.nxtbook.fr/newpress/jeccomposites/jcm1704_112
https://www.nxtbook.fr/newpress/jeccomposites/jcm1703_111
https://www.nxtbook.fr/newpress/jeccomposites/jcm1701_110
https://www.nxtbook.fr/newpress/jeccomposites/jcm1611_109
https://www.nxtbook.fr/newpress/jeccomposites/jcm1610_108
https://www.nxtbook.fr/newpress/jeccomposites/jcm1608_107
https://www.nxtbook.fr/newpress/jeccomposites/jcm1607_106
https://www.nxtbook.fr/newpress/jeccomposites/jcm1605_105
https://www.nxtbook.fr/newpress/jeccomposites/jcm1604_104
https://www.nxtbook.fr/newpress/jeccomposites/jcm1603_103
https://www.nxtbook.fr/newpress/jeccomposites/jcm1601_102
https://www.nxtbook.fr/newpress/jeccomposites/jcm1511_101
https://www.nxtbook.fr/newpress/jeccomposites/jcm1510_100
https://www.nxtbook.fr/newpress/jeccomposites/jcm1509_99
https://www.nxtbook.fr/newpress/jeccomposites/jcm1507_98
https://www.nxtbook.fr/newpress/jeccomposites/jcm1505_97
https://www.nxtbook.fr/newpress/jeccomposites/jcm1504_96
https://www.nxtbook.com/newpress/jeccomposites/jcm1503_95
https://www.nxtbook.com/newpress/jeccomposites/jcm1501_94
https://www.nxtbook.com/newpress/jeccomposites/jcm1412_93
https://www.nxtbook.com/newpress/jeccomposites/jcm1410_92
https://www.nxtbook.com/newpress/jeccomposites/jcm1409_91
https://www.nxtbook.com/newpress/jeccomposites/jcm1406_90
https://www.nxtbook.com/newpress/jeccomposites/jcm1405_89
https://www.nxtbook.com/newpress/jeccomposites/jcm1404_88
https://www.nxtbook.com/newpress/jeccomposites/jcm1403_87
https://www.nxtbook.com/newpress/jeccomposites/jcm1401_86
https://www.nxtbook.com/newpress/jeccomposites/jcm1311_85
https://www.nxtbook.com/newpress/jeccomposites/jcm1310_84
https://www.nxtbook.com/newpress/jeccomposites/jcm1308_83
https://www.nxtbook.com/newpress/jeccomposites/jcm1307_82
https://www.nxtbook.com/newpress/jeccomposites/jcm1305_81
https://www.nxtbook.com/newpress/jeccomposites/jcm1304_80
https://www.nxtbook.com/newpress/jeccomposites/jcm1303_79
https://www.nxtbook.com/newpress/jeccomposites/jcm1301_78
https://www.nxtbook.com/newpress/jeccomposites/jcm1212_77
https://www.nxtbook.com/newpress/jeccomposites/jcm1210_76
https://www.nxtbook.com/newpress/jeccomposites/jcm1208_75
https://www.nxtbook.com/newpress/jeccomposites/jcm1207_74
https://www.nxtbook.com/newpress/jeccomposites/jcm1206_73
https://www.nxtbook.com/newpress/jeccomposites/jcm1204_72
https://www.nxtbook.com/newpress/jeccomposites/jcm1203_71
https://www.nxtbook.com/newpress/jeccomposites/jcm1201_70
https://www.nxtbook.com/newpress/jeccomposites/jcm1111_69
https://www.nxtbook.com/newpress/jeccomposites/jcm1110_68
https://www.nxtbook.com/newpress/jeccomposites/jcm1108_67
https://www.nxtbook.com/newpress/jeccomposites/jcm1107_66
https://www.nxtbook.com/newpress/jeccomposites/jcm1105_65
https://www.nxtbook.com/newpress/jeccomposites/jcm1104_64
https://www.nxtbook.com/newpress/jeccomposites/jcm1103_63
https://www.nxtbook.com/newpress/jeccomposites/jcm1101_62
https://www.nxtbook.com/newpress/jeccomposites/jcm1011_61
https://www.nxtbook.com/newpress/jeccomposites/jcm1010_60
https://www.nxtbook.com/newpress/jeccomposites/jcm1009_59
https://www.nxtbook.com/newpress/jeccomposites/jcm1006_58
https://www.nxtbook.com/newpress/jeccomposites/jcm1005_57
https://www.nxtbook.com/newpress/jeccomposites/jcm1004_56
https://www.nxtbook.com/newpress/jeccomposites/jcm1003_55
https://www.nxtbook.com/newpress/jeccomposites/jcm1001_54
https://www.nxtbook.com/newpress/jeccomposites/jcm0911_53
https://www.nxtbook.com/newpress/jeccomposites/jcm0910_52
https://www.nxtbook.com/newpress/jeccomposites/jcm0909_51
https://www.nxtbook.com/newpress/jeccomposites/jcm0907-08_50
https://www.nxtbook.com/newpress/jeccomposites/jcm0906_49
https://www.nxtbook.com/newpress/jeccomposites/jcm0904_48
https://www.nxtbook.com/newpress/jeccomposites/jcm0903_47
https://www.nxtbook.com/newpress/jeccomposites/jcm0901_46
https://www.nxtbook.com/newpress/jeccomposites/jcm0811_45
https://www.nxtbook.com/newpress/jeccomposites/jcm0810_44
https://www.nxtbook.com/newpress/jeccomposites/jcm0809_43
https://www.nxtbook.com/newpress/jeccomposites/jcm0807_42
https://www.nxtbook.com/newpress/jeccomposites/jcm0806_41
https://www.nxtbook.com/newpress/jeccomposites/jcm0805_40
https://www.nxtbook.com/newpress/jeccomposites/jcm0803_39
https://www.nxtbook.com/newpress/jeccomposites/jcm0801_38
https://www.nxtbook.com/newpress/jeccomposites/jcm0712_37
https://www.nxtbook.com/newpress/jeccomposites/jcm0710_36
https://www.nxtbook.com/newpress/jeccomposites/jcm0709_35
https://www.nxtbook.com/newpress/jeccomposites/jcm0707_34
https://www.nxtbook.com/newpress/jeccomposites/jcm0706_33
https://www.nxtbookmedia.com