JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 57

Adhesion properties of bonded composite-to-aluminium joints using peel tests

Fig. 3: Examples of load-displacement
graphs measured during the peel tests
- (a) FM 73 and (b) EA 9695

temperature. A total of three specimens were tested under
each test condition. During the tests, the load and the crosshead displacement were recorded for every 0.1 s and 0.1 mm,
respectively.

Results
The average peel load and the failure mechanism of the specimens tested are given in Table 3. The average peel load values are shown as the mean standard deviation of the three
specimens tested under each test condition.
Three types of failure mechanisms were observed: cohesive
failure (CF) within the adhesive, adhesive failure (AF) and
intralaminar failure of the composite adherend (ILFC). The
percentage of failure is an estimate based on visual observation of the specimens' failure surface after testing. Figure 3
shows examples of load-displacement curves measured during the peel tests. The average peel load was determined for
150 mm of peeling, regardless of the first 15 mm after a first
peak (decrease of about 5%).
Looking at the results for the standard condition aluminium-to-aluminium (A-a), FM 73 has a good peel performance
(100% CF), and in agreement with the manufacturer's TDS
(Table 1). Although is not specifically mentioned in the
TDS, it is assumed that the peel load performance is given
for 100% CF. On the contrary, EA 9695 performed worse
than expected. The peel load was lower than mentioned in
the TDS, most probably due to the 45% of poor adhesion
(AF) observed in the specimens.
When instead of peeling a flexible aluminium sheet from an
aluminium rigid sheet (A-a), one peels a flexible aluminium
sheet from a CFRP rigid panel (C-a), the results are comparable with the standard condition. The FM 73 peel load decreases by about 20% on C-a when compared to A-a, which
might be caused by the slight decrease of the cohesion failure percentage (from 100% to 95%). Taking into account
that both specimens, A-a and C-a, have comparable CF percentages, the fact that aluminium's coefficient of thermal expansion is significantly different from CFRP's can also play
an important role in the peel load. The residual stresses that

Fig. 4: Load-displacement curves of the FM 73 specimens and the corresponding
failure surfaces of the rigid adherends (a) when peeling off the aluminium and (b)
when peeling off the composite

build up in the adhesive bond line during cooling down can
reduce the peel load from A-a tests to C-a tests.
On the contrary, in the EA 9695 A-a to C-a specimens, the

N°137 November - December 2020

/ jec composites magazine

57



JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020

Table of Contents for the Digital Edition of JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020

Cover
Edito
“We can change the way we envision global shipping overall”
Contents
NEWS
In brief
Agenda
BUSINESS
Human ressources - Skills requirements in the composite materials sector – the French example
Startup - Make lightness and performance affordable without compromising the environment
Offshore - GWEC: Asia Pacific to become the largest offshore wind market by 2030
MANUFACTURING
Additive manufacturing - The METHOD platform expands to support more materials,applications, and markets
Automation - One-shot manufacturing of cylindrical lattice structures for satellite applications
Recycling - World’s first fully-recycled thermoplastic composite application in aerospace
Additive molding - From large-scale continuous thermoplastic composites to mass production
FEATURE AUTOMOTIVE - Is it possible to do better?
FRP - Fully coupled processstructure analysis for automotive center floor panel
Honeycomb - Composite materials for lighter vehicles
Additive manufacturing - Transforming composite production processes with FDM additive manufacturing
EV - All-composite EV wheel moves to next development phase with pilot production
Security - The world’s fastest armoured car
Natural fibre - Sustainable composite solution for new Toyota LQ concept car
SOLUTIONS
Defence - Drones as wingmen
City - Composites for tomorrow’s cities
Maintenance - Degradation mechanism and maintenance of GFRP hydrochloric acid storage tanks
TECHNOLOGY
Bonding - Adhesion properties of bonded composite-to-aluminium joints using peel tests
Inside the lab - The University of Southern Queensland - Centre for Future Materials
Method - Weight and cost reduction with double-double laminates
Index
Advertisers
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - Cover
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 2
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - Edito
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - “We can change the way we envision global shipping overall”
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 5
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - Contents
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 7
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - In brief
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 9
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - Agenda
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - Human ressources - Skills requirements in the composite materials sector – the French example
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 12
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 13
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - Startup - Make lightness and performance affordable without compromising the environment
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 15
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 16
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - Offshore - GWEC: Asia Pacific to become the largest offshore wind market by 2030
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 18
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - Additive manufacturing - The METHOD platform expands to support more materials,applications, and markets
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 20
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - Automation - One-shot manufacturing of cylindrical lattice structures for satellite applications
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 22
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 23
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - Recycling - World’s first fully-recycled thermoplastic composite application in aerospace
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 25
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 26
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - Additive molding - From large-scale continuous thermoplastic composites to mass production
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 28
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 29
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - FRP - Fully coupled processstructure analysis for automotive center floor panel
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 31
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 32
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 33
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - Honeycomb - Composite materials for lighter vehicles
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 35
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 36
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - Additive manufacturing - Transforming composite production processes with FDM additive manufacturing
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 38
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - EV - All-composite EV wheel moves to next development phase with pilot production
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 40
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - Security - The world’s fastest armoured car
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 42
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 43
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - Natural fibre - Sustainable composite solution for new Toyota LQ concept car
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 45
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 46
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - Defence - Drones as wingmen
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 48
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 49
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - City - Composites for tomorrow’s cities
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 51
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - Maintenance - Degradation mechanism and maintenance of GFRP hydrochloric acid storage tanks
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 53
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - Bonding - Adhesion properties of bonded composite-to-aluminium joints using peel tests
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 55
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 56
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 57
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 58
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 59
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 60
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 61
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - Inside the lab - The University of Southern Queensland - Centre for Future Materials
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 63
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - Method - Weight and cost reduction with double-double laminates
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 65
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - Advertisers
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 67
JEC COMPOSITES MAGAZINE - Issue #137 - November/December 2020 - 68
https://www.nxtbook.fr/newpress/jeccomposites/jcm211_143
https://www.nxtbook.fr/newpress/jeccomposites/jcm2109_142
https://www.nxtbook.fr/newpress/jeccomposites/jcm2107_141
https://www.nxtbook.fr/newpress/jeccomposites/jcm2105_140
https://www.nxtbook.fr/newpress/jeccomposites/jcm2103_139
https://www.nxtbook.fr/newpress/jeccomposites/jcm-experts-digest-additive-manufacturing-2020
https://www.nxtbook.fr/newpress/jeccomposites/jcm2101_138
https://www.nxtbook.fr/newpress/jeccomposites/jcm2011_Special_Issue4
https://www.nxtbook.fr/newpress/jeccomposites/jcm2011_137
https://www.nxtbook.fr/newpress/jeccomposites/jcm2009_136
https://www.nxtbook.fr/newpress/jeccomposites/jcm2007_135
https://www.nxtbook.fr/newpress/jeccomposites/jcm_2020_Q1_Innovation_Report
https://www.nxtbook.fr/newpress/jeccomposites/jcm2005_Special_Issue3
https://www.nxtbook.fr/newpress/jeccomposites/jcm2005_134
https://www.nxtbook.fr/newpress/jeccomposites/jcm2003_133
https://www.nxtbook.fr/newpress/jeccomposites/jcm2001_132
https://www.nxtbook.fr/newpress/jeccomposites/jcm1911_Special_Issue2
https://www.nxtbook.fr/newpress/jeccomposites/jcm1911_131
https://www.nxtbook.fr/newpress/jeccomposites/jcm1909_130
https://www.nxtbook.fr/newpress/jeccomposites/jcm1907_129
https://www.nxtbook.fr/newpress/jeccomposites/jcm1905_128
https://www.nxtbook.fr/newpress/jeccomposites/jcm1903_Special_Issue1
https://www.nxtbook.fr/newpress/jeccomposites/jcm1903_127
https://www.nxtbook.fr/newpress/jeccomposites/jcm1901_126
https://www.nxtbook.fr/newpress/jeccomposites/jcm1811_125
https://www.nxtbook.fr/newpress/jeccomposites/jcm1810_124
https://www.nxtbook.fr/newpress/jeccomposites/jcm1808_123
https://www.nxtbook.fr/newpress/jeccomposites/jcm1807_122
https://www.nxtbook.fr/newpress/jeccomposites/jcm1805_121
https://www.nxtbook.fr/newpress/jeccomposites/jcm1804_120
https://www.nxtbook.fr/newpress/jeccomposites/jcm1803_119
https://www.nxtbook.fr/newpress/jeccomposites/jcm1802_119-Supplement_Innovation_Report
https://www.nxtbook.fr/newpress/jeccomposites/jcm1801_118
https://www.nxtbook.fr/newpress/jeccomposites/jcm1711_117
https://www.nxtbook.fr/newpress/jeccomposites/jcm1710_116
https://www.nxtbook.fr/newpress/jeccomposites/jcm1708_115
https://www.nxtbook.fr/newpress/jeccomposites/jcm1707_114
https://www.nxtbook.fr/newpress/jeccomposites/jcm1706_113
https://www.nxtbook.fr/newpress/jeccomposites/jcm1704_112
https://www.nxtbook.fr/newpress/jeccomposites/jcm1703_111
https://www.nxtbook.fr/newpress/jeccomposites/jcm1701_110
https://www.nxtbook.fr/newpress/jeccomposites/jcm1611_109
https://www.nxtbook.fr/newpress/jeccomposites/jcm1610_108
https://www.nxtbook.fr/newpress/jeccomposites/jcm1608_107
https://www.nxtbook.fr/newpress/jeccomposites/jcm1607_106
https://www.nxtbook.fr/newpress/jeccomposites/jcm1605_105
https://www.nxtbook.fr/newpress/jeccomposites/jcm1604_104
https://www.nxtbook.fr/newpress/jeccomposites/jcm1603_103
https://www.nxtbook.fr/newpress/jeccomposites/jcm1601_102
https://www.nxtbook.fr/newpress/jeccomposites/jcm1511_101
https://www.nxtbook.fr/newpress/jeccomposites/jcm1510_100
https://www.nxtbook.fr/newpress/jeccomposites/jcm1509_99
https://www.nxtbook.fr/newpress/jeccomposites/jcm1507_98
https://www.nxtbook.fr/newpress/jeccomposites/jcm1505_97
https://www.nxtbook.fr/newpress/jeccomposites/jcm1504_96
https://www.nxtbook.com/newpress/jeccomposites/jcm1503_95
https://www.nxtbook.com/newpress/jeccomposites/jcm1501_94
https://www.nxtbook.com/newpress/jeccomposites/jcm1412_93
https://www.nxtbook.com/newpress/jeccomposites/jcm1410_92
https://www.nxtbook.com/newpress/jeccomposites/jcm1409_91
https://www.nxtbook.com/newpress/jeccomposites/jcm1406_90
https://www.nxtbook.com/newpress/jeccomposites/jcm1405_89
https://www.nxtbook.com/newpress/jeccomposites/jcm1404_88
https://www.nxtbook.com/newpress/jeccomposites/jcm1403_87
https://www.nxtbook.com/newpress/jeccomposites/jcm1401_86
https://www.nxtbook.com/newpress/jeccomposites/jcm1311_85
https://www.nxtbook.com/newpress/jeccomposites/jcm1310_84
https://www.nxtbook.com/newpress/jeccomposites/jcm1308_83
https://www.nxtbook.com/newpress/jeccomposites/jcm1307_82
https://www.nxtbook.com/newpress/jeccomposites/jcm1305_81
https://www.nxtbook.com/newpress/jeccomposites/jcm1304_80
https://www.nxtbook.com/newpress/jeccomposites/jcm1303_79
https://www.nxtbook.com/newpress/jeccomposites/jcm1301_78
https://www.nxtbook.com/newpress/jeccomposites/jcm1212_77
https://www.nxtbook.com/newpress/jeccomposites/jcm1210_76
https://www.nxtbook.com/newpress/jeccomposites/jcm1208_75
https://www.nxtbook.com/newpress/jeccomposites/jcm1207_74
https://www.nxtbook.com/newpress/jeccomposites/jcm1206_73
https://www.nxtbook.com/newpress/jeccomposites/jcm1204_72
https://www.nxtbook.com/newpress/jeccomposites/jcm1203_71
https://www.nxtbook.com/newpress/jeccomposites/jcm1201_70
https://www.nxtbook.com/newpress/jeccomposites/jcm1111_69
https://www.nxtbook.com/newpress/jeccomposites/jcm1110_68
https://www.nxtbook.com/newpress/jeccomposites/jcm1108_67
https://www.nxtbook.com/newpress/jeccomposites/jcm1107_66
https://www.nxtbook.com/newpress/jeccomposites/jcm1105_65
https://www.nxtbook.com/newpress/jeccomposites/jcm1104_64
https://www.nxtbook.com/newpress/jeccomposites/jcm1103_63
https://www.nxtbook.com/newpress/jeccomposites/jcm1101_62
https://www.nxtbook.com/newpress/jeccomposites/jcm1011_61
https://www.nxtbook.com/newpress/jeccomposites/jcm1010_60
https://www.nxtbook.com/newpress/jeccomposites/jcm1009_59
https://www.nxtbook.com/newpress/jeccomposites/jcm1006_58
https://www.nxtbook.com/newpress/jeccomposites/jcm1005_57
https://www.nxtbook.com/newpress/jeccomposites/jcm1004_56
https://www.nxtbook.com/newpress/jeccomposites/jcm1003_55
https://www.nxtbook.com/newpress/jeccomposites/jcm1001_54
https://www.nxtbook.com/newpress/jeccomposites/jcm0911_53
https://www.nxtbook.com/newpress/jeccomposites/jcm0910_52
https://www.nxtbook.com/newpress/jeccomposites/jcm0909_51
https://www.nxtbook.com/newpress/jeccomposites/jcm0907-08_50
https://www.nxtbook.com/newpress/jeccomposites/jcm0906_49
https://www.nxtbook.com/newpress/jeccomposites/jcm0904_48
https://www.nxtbook.com/newpress/jeccomposites/jcm0903_47
https://www.nxtbook.com/newpress/jeccomposites/jcm0901_46
https://www.nxtbook.com/newpress/jeccomposites/jcm0811_45
https://www.nxtbook.com/newpress/jeccomposites/jcm0810_44
https://www.nxtbook.com/newpress/jeccomposites/jcm0809_43
https://www.nxtbook.com/newpress/jeccomposites/jcm0807_42
https://www.nxtbook.com/newpress/jeccomposites/jcm0806_41
https://www.nxtbook.com/newpress/jeccomposites/jcm0805_40
https://www.nxtbook.com/newpress/jeccomposites/jcm0803_39
https://www.nxtbook.com/newpress/jeccomposites/jcm0801_38
https://www.nxtbook.com/newpress/jeccomposites/jcm0712_37
https://www.nxtbook.com/newpress/jeccomposites/jcm0710_36
https://www.nxtbook.com/newpress/jeccomposites/jcm0709_35
https://www.nxtbook.com/newpress/jeccomposites/jcm0707_34
https://www.nxtbook.com/newpress/jeccomposites/jcm0706_33
https://www.nxtbookmedia.com