JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 94

fabric

Fig. 6: Examples of selected fabric assemblies

between yarns and between the projectile and the fabric. A
fixed edge boundary condition was applied for all the cases and
a projectile velocity of 500 m/s was selected. It was assumed
that the inter-yarn frictional coefficient was 0.2.

Fig. 7: Energy absorption for 2-ply panels

2-ply panels
Figure 7 shows the FEA simulation results from the case of a
2-ply fabric panel. Two velocities, 500 m/s and 300 m/s, were
selected to study how the impact velocity affects the ballistic
impact performance with various fabric assemblies. The results
show that the ply orientations within the fabric assembly significantly affected the energy absorption capacity of ballistic fabrics
and energy absorption was increased as the orientation angle θ
increased. The energy absorption capacity slightly increased as
the impact velocity decreased, as depicted in Figure 7. Compared with the aligned ply panel denoted as [0/0], the energy
absorption in the angled panel [0/45] increased by 11.4 % for a
300 m/s impact velocity and 10% for a 500 m/s impact velocity.
3-ply panels
The results for the 3-ply fabric panels are shown in Figure 8.
The energy absorption capacity increased when the constituent
fabric layers were angle-laid in the plies. The energy absorption
for all the panels with layer orientation was higher than the aligned panel in the angle-laid panel [0/0/0]. The most energy absorbent panel was [0/30/60], absorbing about 16% more than
the aligned panel. It is interesting to note that panels [45/0/0],
[0/45/0] and [0/0/45], one 45° ply involved, demonstrated a
different energy absorption capability, with [0/45/0] being the
most energy absorbent. The results indicate that the position of
the layer had a significant effect on energy absorption. The FE
results also showed the significant effect of ply orientations on
energy absorption.
Figure 9 presents the results for the 4-ply panels. Three impact
velocities were used to investigate the energy absorption performance of these panels. Again, the calculated results demonstrated that the angle-laid panels absorb more energy than the
aligned one at all impact velocities. It is evident that the low

94 jec composites magazine / No79 March 2013

Fig. 8: Energy absorption for 3-ply panels

Fig. 9: Energy absorption for 2-ply panels



JEC COMPOSITES MAGAZINE - Issue #79 - March 2013

Table of Contents for the Digital Edition of JEC COMPOSITES MAGAZINE - Issue #79 - March 2013

Cover
Edito
Point of view: research & industry
Contents
Agenda of Events
COMPANY & BUSINESS
- In brief
- Core materials
APPLICATIONS
- Formula 1
- Equipment
- Wind energy
MARKET
- Europe
- Patents
FEATURE SPECIAL JEC EUROPE 2013
- Turkey, country guest of honor
- 7th International Composites Summit
- JEC Europe lnnovation Awards Programme
- lnnovation report and news
- Sustainability
RESEARCH & DEVELOPMENT
- Additive
- Fabric
TECHNOLOGY & INNOVATIONS
- Process
- Matrix
- Nano
- Resins
- Process
Index
In the world
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - Cover
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 2
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - Edito
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - Point of view: research & industry
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 5
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - Contents
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 7
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 8
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 9
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 10
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 11
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - Agenda of Events
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 13
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 14
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - In brief
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - Ad1
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - Ad2
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 16
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 17
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Core materials
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 19
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 20
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Formula 1
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 22
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 23
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Equipment
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 25
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Wind energy
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 27
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Europe
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 29
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 30
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 31
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 32
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 33
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Patents
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 35
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 36
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 37
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Turkey, country guest of honor
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 39
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 40
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 41
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 42
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 43
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - 7th International Composites Summit
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 45
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 46
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 47
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - JEC Europe lnnovation Awards Programme
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 49
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 50
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 51
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 52
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 53
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 54
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 55
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - lnnovation report and news
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 57
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 58
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 59
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 60
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 61
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 62
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 63
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 64
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 65
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 66
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 67
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 68
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 69
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 70
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 71
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 72
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 73
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 74
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 75
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 76
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 77
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Sustainability
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 79
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 80
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 81
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 82
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 83
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 84
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Additive
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 86
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 87
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 88
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Fabric
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 90
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 91
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 92
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 93
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 94
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 95
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 96
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Process
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 98
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 99
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Matrix
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 101
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 102
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 103
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 104
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Nano
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 106
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 107
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Resins
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 109
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Process
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 111
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 112
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - Index
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - In the world
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 115
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 116
https://www.nxtbook.fr/newpress/jeccomposites/jcm2211_148
https://www.nxtbook.fr/newpress/jeccomposites/jcm2209_147
https://www.nxtbook.fr/newpress/jeccomposites/jcm2206_146
https://www.nxtbook.fr/newpress/jeccomposites/jcm2204_145
https://www.nxtbook.fr/newpress/jeccomposites/jcm2201_144
https://www.nxtbook.fr/newpress/jeccomposites/jcm211_143
https://www.nxtbook.fr/newpress/jeccomposites/jcm2109_142
https://www.nxtbook.fr/newpress/jeccomposites/jcm2107_141
https://www.nxtbook.fr/newpress/jeccomposites/jcm2105_140
https://www.nxtbook.fr/newpress/jeccomposites/jcm2103_139
https://www.nxtbook.fr/newpress/jeccomposites/jcm-experts-digest-additive-manufacturing-2020
https://www.nxtbook.fr/newpress/jeccomposites/jcm2101_138
https://www.nxtbook.fr/newpress/jeccomposites/jcm2011_Special_Issue4
https://www.nxtbook.fr/newpress/jeccomposites/jcm2011_137
https://www.nxtbook.fr/newpress/jeccomposites/jcm2009_136
https://www.nxtbook.fr/newpress/jeccomposites/jcm2007_135
https://www.nxtbook.fr/newpress/jeccomposites/jcm_2020_Q1_Innovation_Report
https://www.nxtbook.fr/newpress/jeccomposites/jcm2005_Special_Issue3
https://www.nxtbook.fr/newpress/jeccomposites/jcm2005_134
https://www.nxtbook.fr/newpress/jeccomposites/jcm2003_133
https://www.nxtbook.fr/newpress/jeccomposites/jcm2001_132
https://www.nxtbook.fr/newpress/jeccomposites/jcm1911_Special_Issue2
https://www.nxtbook.fr/newpress/jeccomposites/jcm1911_131
https://www.nxtbook.fr/newpress/jeccomposites/jcm1909_130
https://www.nxtbook.fr/newpress/jeccomposites/jcm1907_129
https://www.nxtbook.fr/newpress/jeccomposites/jcm1905_128
https://www.nxtbook.fr/newpress/jeccomposites/jcm1903_Special_Issue1
https://www.nxtbook.fr/newpress/jeccomposites/jcm1903_127
https://www.nxtbook.fr/newpress/jeccomposites/jcm1901_126
https://www.nxtbook.fr/newpress/jeccomposites/jcm1811_125
https://www.nxtbook.fr/newpress/jeccomposites/jcm1810_124
https://www.nxtbook.fr/newpress/jeccomposites/jcm1808_123
https://www.nxtbook.fr/newpress/jeccomposites/jcm1807_122
https://www.nxtbook.fr/newpress/jeccomposites/jcm1805_121
https://www.nxtbook.fr/newpress/jeccomposites/jcm1804_120
https://www.nxtbook.fr/newpress/jeccomposites/jcm1803_119
https://www.nxtbook.fr/newpress/jeccomposites/jcm1802_119-Supplement_Innovation_Report
https://www.nxtbook.fr/newpress/jeccomposites/jcm1801_118
https://www.nxtbook.fr/newpress/jeccomposites/jcm1711_117
https://www.nxtbook.fr/newpress/jeccomposites/jcm1710_116
https://www.nxtbook.fr/newpress/jeccomposites/jcm1708_115
https://www.nxtbook.fr/newpress/jeccomposites/jcm1707_114
https://www.nxtbook.fr/newpress/jeccomposites/jcm1706_113
https://www.nxtbook.fr/newpress/jeccomposites/jcm1704_112
https://www.nxtbook.fr/newpress/jeccomposites/jcm1703_111
https://www.nxtbook.fr/newpress/jeccomposites/jcm1701_110
https://www.nxtbook.fr/newpress/jeccomposites/jcm1611_109
https://www.nxtbook.fr/newpress/jeccomposites/jcm1610_108
https://www.nxtbook.fr/newpress/jeccomposites/jcm1608_107
https://www.nxtbook.fr/newpress/jeccomposites/jcm1607_106
https://www.nxtbook.fr/newpress/jeccomposites/jcm1605_105
https://www.nxtbook.fr/newpress/jeccomposites/jcm1604_104
https://www.nxtbook.fr/newpress/jeccomposites/jcm1603_103
https://www.nxtbook.fr/newpress/jeccomposites/jcm1601_102
https://www.nxtbook.fr/newpress/jeccomposites/jcm1511_101
https://www.nxtbook.fr/newpress/jeccomposites/jcm1510_100
https://www.nxtbook.fr/newpress/jeccomposites/jcm1509_99
https://www.nxtbook.fr/newpress/jeccomposites/jcm1507_98
https://www.nxtbook.fr/newpress/jeccomposites/jcm1505_97
https://www.nxtbook.fr/newpress/jeccomposites/jcm1504_96
https://www.nxtbook.com/newpress/jeccomposites/jcm1503_95
https://www.nxtbook.com/newpress/jeccomposites/jcm1501_94
https://www.nxtbook.com/newpress/jeccomposites/jcm1412_93
https://www.nxtbook.com/newpress/jeccomposites/jcm1410_92
https://www.nxtbook.com/newpress/jeccomposites/jcm1409_91
https://www.nxtbook.com/newpress/jeccomposites/jcm1406_90
https://www.nxtbook.com/newpress/jeccomposites/jcm1405_89
https://www.nxtbook.com/newpress/jeccomposites/jcm1404_88
https://www.nxtbook.com/newpress/jeccomposites/jcm1403_87
https://www.nxtbook.com/newpress/jeccomposites/jcm1401_86
https://www.nxtbook.com/newpress/jeccomposites/jcm1311_85
https://www.nxtbook.com/newpress/jeccomposites/jcm1310_84
https://www.nxtbook.com/newpress/jeccomposites/jcm1308_83
https://www.nxtbook.com/newpress/jeccomposites/jcm1307_82
https://www.nxtbook.com/newpress/jeccomposites/jcm1305_81
https://www.nxtbook.com/newpress/jeccomposites/jcm1304_80
https://www.nxtbook.com/newpress/jeccomposites/jcm1303_79
https://www.nxtbook.com/newpress/jeccomposites/jcm1301_78
https://www.nxtbook.com/newpress/jeccomposites/jcm1212_77
https://www.nxtbook.com/newpress/jeccomposites/jcm1210_76
https://www.nxtbook.com/newpress/jeccomposites/jcm1208_75
https://www.nxtbook.com/newpress/jeccomposites/jcm1207_74
https://www.nxtbook.com/newpress/jeccomposites/jcm1206_73
https://www.nxtbook.com/newpress/jeccomposites/jcm1204_72
https://www.nxtbook.com/newpress/jeccomposites/jcm1203_71
https://www.nxtbook.com/newpress/jeccomposites/jcm1201_70
https://www.nxtbook.com/newpress/jeccomposites/jcm1111_69
https://www.nxtbook.com/newpress/jeccomposites/jcm1110_68
https://www.nxtbook.com/newpress/jeccomposites/jcm1108_67
https://www.nxtbook.com/newpress/jeccomposites/jcm1107_66
https://www.nxtbook.com/newpress/jeccomposites/jcm1105_65
https://www.nxtbook.com/newpress/jeccomposites/jcm1104_64
https://www.nxtbook.com/newpress/jeccomposites/jcm1103_63
https://www.nxtbook.com/newpress/jeccomposites/jcm1101_62
https://www.nxtbook.com/newpress/jeccomposites/jcm1011_61
https://www.nxtbook.com/newpress/jeccomposites/jcm1010_60
https://www.nxtbook.com/newpress/jeccomposites/jcm1009_59
https://www.nxtbook.com/newpress/jeccomposites/jcm1006_58
https://www.nxtbook.com/newpress/jeccomposites/jcm1005_57
https://www.nxtbook.com/newpress/jeccomposites/jcm1004_56
https://www.nxtbook.com/newpress/jeccomposites/jcm1003_55
https://www.nxtbook.com/newpress/jeccomposites/jcm1001_54
https://www.nxtbook.com/newpress/jeccomposites/jcm0911_53
https://www.nxtbook.com/newpress/jeccomposites/jcm0910_52
https://www.nxtbook.com/newpress/jeccomposites/jcm0909_51
https://www.nxtbook.com/newpress/jeccomposites/jcm0907-08_50
https://www.nxtbook.com/newpress/jeccomposites/jcm0906_49
https://www.nxtbook.com/newpress/jeccomposites/jcm0904_48
https://www.nxtbook.com/newpress/jeccomposites/jcm0903_47
https://www.nxtbook.com/newpress/jeccomposites/jcm0901_46
https://www.nxtbook.com/newpress/jeccomposites/jcm0811_45
https://www.nxtbook.com/newpress/jeccomposites/jcm0810_44
https://www.nxtbook.com/newpress/jeccomposites/jcm0809_43
https://www.nxtbook.com/newpress/jeccomposites/jcm0807_42
https://www.nxtbook.com/newpress/jeccomposites/jcm0806_41
https://www.nxtbook.com/newpress/jeccomposites/jcm0805_40
https://www.nxtbook.com/newpress/jeccomposites/jcm0803_39
https://www.nxtbook.com/newpress/jeccomposites/jcm0801_38
https://www.nxtbook.com/newpress/jeccomposites/jcm0712_37
https://www.nxtbook.com/newpress/jeccomposites/jcm0710_36
https://www.nxtbook.com/newpress/jeccomposites/jcm0709_35
https://www.nxtbook.com/newpress/jeccomposites/jcm0707_34
https://www.nxtbook.com/newpress/jeccomposites/jcm0706_33
https://www.nxtbookmedia.com