JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 92

fabric
added cost. This structure ensures that the fabric is woven using
the optimised weave but with extra gripping on the constituent
yarns. Yarn pulling-out tests were carried out in order to examine the effectiveness of the structure used in GRPG-1.

gripping to its constituent yarns. The first samples of this type
of fabric were developed based on hand-loom weaving. The
fabric can be manufactured on power looms with minor and
necessary modifications to the loom.

Experimental evaluation of 2D fabrics
Yarn gripping effectiveness
For comparison purposes, the 2D broad fabric with enhanced
yarn gripping, GRPG-1, was tested and compared with four
narrow fabrics with natural selvedge, which were shown to
be advantageous over the fabric stripes without weft yarn
gripping [17]. All fabrics were evaluated on the amount of
materials needed to stop the projectile and on the depth of the
backface signature. Figure 2 shows a comparison between the
two groups of ballistic fabrics.

Fig. 1: Resistance to yarn pull-out from GRPG-1 fabric

Figure 1 shows the load-displacement relationship between
the plain and GRPG-1 ballistic fabrics. The GRPG-1 fabric
demonstrates higher resistance to yarn pull-out during the
process. It is noted that the GRPG-1 fabric offers 40% more
resistance than its plain counterpart. According to Lyons [11],
fabrics with this feature would contribute to faster longitudinal propagation and therefore would dissipate impact energy
more effectively. After the yarn was pulled out from the fabric,
the plain fabric and the GRPG-1 fabric demonstrated similar
yarn movement with similar resistance. This is advantageous
for the GRPG-1 fabrics as it shows that, despite the tighter
gripping on yarns, the new fabric also permits the necessary
yarn displacement during fabric deformation to absorb impact
energy.
GRPG-2 is another 2D woven fabric that offers enhanced

From the study on narrow fabrics, it was concluded that
narrow fabrics with natural selvedge demonstrated better
ballistic properties than their narrow stripe counterparts
[Cork and Forster][Sun and Chen]. However, the problem of
narrow fabrics for ballistic protection is that they cannot offer
the material continuity required for impact energy dissipation. GRPG-1, as an engineered fabric, offers both material
continuity and extra yarn gripping. Figure 1(a) compares the
two types of fabrics on the areal density needed to block the
projectile under different levels of impact energy. It shows
that the GRPG-1 fabric can stop the impacting projectile with
almost the lowest areal density regardless of the impact energy
applied. Figure 5(b) shows clearly that the GRPG-1 fabric
is the best in absorbing and dissipating the residual impact
energy as it relates to the smallest depth of backface signature.
To summarise, the engineered GRPG-1 fabric based on the
new engineering concept out-performs the narrow fabrics
with natural selvedge and is a strong candidate material for
ballistic protection.

Fig. 2: GRPG-1 vs narrow fabrics: (right) Materials needed to stop penetration, (left) Depth of backface signature

92 jec composites magazine / No79 March 2013



JEC COMPOSITES MAGAZINE - Issue #79 - March 2013

Table of Contents for the Digital Edition of JEC COMPOSITES MAGAZINE - Issue #79 - March 2013

Cover
Edito
Point of view: research & industry
Contents
Agenda of Events
COMPANY & BUSINESS
- In brief
- Core materials
APPLICATIONS
- Formula 1
- Equipment
- Wind energy
MARKET
- Europe
- Patents
FEATURE SPECIAL JEC EUROPE 2013
- Turkey, country guest of honor
- 7th International Composites Summit
- JEC Europe lnnovation Awards Programme
- lnnovation report and news
- Sustainability
RESEARCH & DEVELOPMENT
- Additive
- Fabric
TECHNOLOGY & INNOVATIONS
- Process
- Matrix
- Nano
- Resins
- Process
Index
In the world
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - Cover
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 2
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - Edito
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - Point of view: research & industry
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 5
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - Contents
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 7
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 8
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 9
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 10
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 11
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - Agenda of Events
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 13
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 14
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - In brief
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - Ad1
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - Ad2
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 16
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 17
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Core materials
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 19
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 20
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Formula 1
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 22
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 23
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Equipment
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 25
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Wind energy
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 27
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Europe
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 29
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 30
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 31
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 32
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 33
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Patents
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 35
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 36
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 37
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Turkey, country guest of honor
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 39
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 40
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 41
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 42
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 43
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - 7th International Composites Summit
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 45
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 46
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 47
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - JEC Europe lnnovation Awards Programme
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 49
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 50
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 51
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 52
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 53
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 54
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 55
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - lnnovation report and news
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 57
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 58
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 59
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 60
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 61
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 62
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 63
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 64
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 65
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 66
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 67
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 68
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 69
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 70
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 71
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 72
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 73
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 74
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 75
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 76
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 77
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Sustainability
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 79
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 80
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 81
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 82
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 83
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 84
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Additive
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 86
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 87
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 88
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Fabric
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 90
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 91
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 92
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 93
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 94
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 95
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 96
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Process
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 98
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 99
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Matrix
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 101
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 102
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 103
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 104
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Nano
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 106
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 107
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Resins
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 109
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - - Process
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 111
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 112
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - Index
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - In the world
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 115
JEC COMPOSITES MAGAZINE - Issue #79 - March 2013 - 116
https://www.nxtbook.fr/newpress/jeccomposites/jcm2109_142
https://www.nxtbook.fr/newpress/jeccomposites/jcm2107_141
https://www.nxtbook.fr/newpress/jeccomposites/jcm2105_140
https://www.nxtbook.fr/newpress/jeccomposites/jcm2103_139
https://www.nxtbook.fr/newpress/jeccomposites/jcm-experts-digest-additive-manufacturing-2020
https://www.nxtbook.fr/newpress/jeccomposites/jcm2101_138
https://www.nxtbook.fr/newpress/jeccomposites/jcm2011_Special_Issue4
https://www.nxtbook.fr/newpress/jeccomposites/jcm2011_137
https://www.nxtbook.fr/newpress/jeccomposites/jcm2009_136
https://www.nxtbook.fr/newpress/jeccomposites/jcm2007_135
https://www.nxtbook.fr/newpress/jeccomposites/jcm_2020_Q1_Innovation_Report
https://www.nxtbook.fr/newpress/jeccomposites/jcm2005_Special_Issue3
https://www.nxtbook.fr/newpress/jeccomposites/jcm2005_134
https://www.nxtbook.fr/newpress/jeccomposites/jcm2003_133
https://www.nxtbook.fr/newpress/jeccomposites/jcm2001_132
https://www.nxtbook.fr/newpress/jeccomposites/jcm1911_Special_Issue2
https://www.nxtbook.fr/newpress/jeccomposites/jcm1911_131
https://www.nxtbook.fr/newpress/jeccomposites/jcm1909_130
https://www.nxtbook.fr/newpress/jeccomposites/jcm1907_129
https://www.nxtbook.fr/newpress/jeccomposites/jcm1905_128
https://www.nxtbook.fr/newpress/jeccomposites/jcm1903_Special_Issue1
https://www.nxtbook.fr/newpress/jeccomposites/jcm1903_127
https://www.nxtbook.fr/newpress/jeccomposites/jcm1901_126
https://www.nxtbook.fr/newpress/jeccomposites/jcm1811_125
https://www.nxtbook.fr/newpress/jeccomposites/jcm1810_124
https://www.nxtbook.fr/newpress/jeccomposites/jcm1808_123
https://www.nxtbook.fr/newpress/jeccomposites/jcm1807_122
https://www.nxtbook.fr/newpress/jeccomposites/jcm1805_121
https://www.nxtbook.fr/newpress/jeccomposites/jcm1804_120
https://www.nxtbook.fr/newpress/jeccomposites/jcm1803_119
https://www.nxtbook.fr/newpress/jeccomposites/jcm1802_119-Supplement_Innovation_Report
https://www.nxtbook.fr/newpress/jeccomposites/jcm1801_118
https://www.nxtbook.fr/newpress/jeccomposites/jcm1711_117
https://www.nxtbook.fr/newpress/jeccomposites/jcm1710_116
https://www.nxtbook.fr/newpress/jeccomposites/jcm1708_115
https://www.nxtbook.fr/newpress/jeccomposites/jcm1707_114
https://www.nxtbook.fr/newpress/jeccomposites/jcm1706_113
https://www.nxtbook.fr/newpress/jeccomposites/jcm1704_112
https://www.nxtbook.fr/newpress/jeccomposites/jcm1703_111
https://www.nxtbook.fr/newpress/jeccomposites/jcm1701_110
https://www.nxtbook.fr/newpress/jeccomposites/jcm1611_109
https://www.nxtbook.fr/newpress/jeccomposites/jcm1610_108
https://www.nxtbook.fr/newpress/jeccomposites/jcm1608_107
https://www.nxtbook.fr/newpress/jeccomposites/jcm1607_106
https://www.nxtbook.fr/newpress/jeccomposites/jcm1605_105
https://www.nxtbook.fr/newpress/jeccomposites/jcm1604_104
https://www.nxtbook.fr/newpress/jeccomposites/jcm1603_103
https://www.nxtbook.fr/newpress/jeccomposites/jcm1601_102
https://www.nxtbook.fr/newpress/jeccomposites/jcm1511_101
https://www.nxtbook.fr/newpress/jeccomposites/jcm1510_100
https://www.nxtbook.fr/newpress/jeccomposites/jcm1509_99
https://www.nxtbook.fr/newpress/jeccomposites/jcm1507_98
https://www.nxtbook.fr/newpress/jeccomposites/jcm1505_97
https://www.nxtbook.fr/newpress/jeccomposites/jcm1504_96
https://www.nxtbook.com/newpress/jeccomposites/jcm1503_95
https://www.nxtbook.com/newpress/jeccomposites/jcm1501_94
https://www.nxtbook.com/newpress/jeccomposites/jcm1412_93
https://www.nxtbook.com/newpress/jeccomposites/jcm1410_92
https://www.nxtbook.com/newpress/jeccomposites/jcm1409_91
https://www.nxtbook.com/newpress/jeccomposites/jcm1406_90
https://www.nxtbook.com/newpress/jeccomposites/jcm1405_89
https://www.nxtbook.com/newpress/jeccomposites/jcm1404_88
https://www.nxtbook.com/newpress/jeccomposites/jcm1403_87
https://www.nxtbook.com/newpress/jeccomposites/jcm1401_86
https://www.nxtbook.com/newpress/jeccomposites/jcm1311_85
https://www.nxtbook.com/newpress/jeccomposites/jcm1310_84
https://www.nxtbook.com/newpress/jeccomposites/jcm1308_83
https://www.nxtbook.com/newpress/jeccomposites/jcm1307_82
https://www.nxtbook.com/newpress/jeccomposites/jcm1305_81
https://www.nxtbook.com/newpress/jeccomposites/jcm1304_80
https://www.nxtbook.com/newpress/jeccomposites/jcm1303_79
https://www.nxtbook.com/newpress/jeccomposites/jcm1301_78
https://www.nxtbook.com/newpress/jeccomposites/jcm1212_77
https://www.nxtbook.com/newpress/jeccomposites/jcm1210_76
https://www.nxtbook.com/newpress/jeccomposites/jcm1208_75
https://www.nxtbook.com/newpress/jeccomposites/jcm1207_74
https://www.nxtbook.com/newpress/jeccomposites/jcm1206_73
https://www.nxtbook.com/newpress/jeccomposites/jcm1204_72
https://www.nxtbook.com/newpress/jeccomposites/jcm1203_71
https://www.nxtbook.com/newpress/jeccomposites/jcm1201_70
https://www.nxtbook.com/newpress/jeccomposites/jcm1111_69
https://www.nxtbook.com/newpress/jeccomposites/jcm1110_68
https://www.nxtbook.com/newpress/jeccomposites/jcm1108_67
https://www.nxtbook.com/newpress/jeccomposites/jcm1107_66
https://www.nxtbook.com/newpress/jeccomposites/jcm1105_65
https://www.nxtbook.com/newpress/jeccomposites/jcm1104_64
https://www.nxtbook.com/newpress/jeccomposites/jcm1103_63
https://www.nxtbook.com/newpress/jeccomposites/jcm1101_62
https://www.nxtbook.com/newpress/jeccomposites/jcm1011_61
https://www.nxtbook.com/newpress/jeccomposites/jcm1010_60
https://www.nxtbook.com/newpress/jeccomposites/jcm1009_59
https://www.nxtbook.com/newpress/jeccomposites/jcm1006_58
https://www.nxtbook.com/newpress/jeccomposites/jcm1005_57
https://www.nxtbook.com/newpress/jeccomposites/jcm1004_56
https://www.nxtbook.com/newpress/jeccomposites/jcm1003_55
https://www.nxtbook.com/newpress/jeccomposites/jcm1001_54
https://www.nxtbook.com/newpress/jeccomposites/jcm0911_53
https://www.nxtbook.com/newpress/jeccomposites/jcm0910_52
https://www.nxtbook.com/newpress/jeccomposites/jcm0909_51
https://www.nxtbook.com/newpress/jeccomposites/jcm0907-08_50
https://www.nxtbook.com/newpress/jeccomposites/jcm0906_49
https://www.nxtbook.com/newpress/jeccomposites/jcm0904_48
https://www.nxtbook.com/newpress/jeccomposites/jcm0903_47
https://www.nxtbook.com/newpress/jeccomposites/jcm0901_46
https://www.nxtbook.com/newpress/jeccomposites/jcm0811_45
https://www.nxtbook.com/newpress/jeccomposites/jcm0810_44
https://www.nxtbook.com/newpress/jeccomposites/jcm0809_43
https://www.nxtbook.com/newpress/jeccomposites/jcm0807_42
https://www.nxtbook.com/newpress/jeccomposites/jcm0806_41
https://www.nxtbook.com/newpress/jeccomposites/jcm0805_40
https://www.nxtbook.com/newpress/jeccomposites/jcm0803_39
https://www.nxtbook.com/newpress/jeccomposites/jcm0801_38
https://www.nxtbook.com/newpress/jeccomposites/jcm0712_37
https://www.nxtbook.com/newpress/jeccomposites/jcm0710_36
https://www.nxtbook.com/newpress/jeccomposites/jcm0709_35
https://www.nxtbook.com/newpress/jeccomposites/jcm0707_34
https://www.nxtbook.com/newpress/jeccomposites/jcm0706_33
https://www.nxtbookmedia.com