JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 43

Fig.2: Tensile test results

Fig.3: Specific properties of NPSP composites

combinations, different fibre architectures were also tested. Fourmm-thick test samples were produced in a two-sided mould using the VARTM technique. Resin, fibre and mould

because they have suitable sizings to promote adhesion. Suitable sizings or other fibre treatments are currently Fig.4: Minimum weight design for stiff plates under were conditioned to development for natural fibres to ensure equal conditions improve their performance in for all samples during composites. An exception is the production. The initial strength and stiffness of the light results are based on tensile architectures (sandwich), which all tests according to ISO have about the same density. In this 527-4. case, the natural sandwich performs Properties were compared better than a glass/foam sandwich. for four different This is an interesting way of thinking. architectures: base In general, structures are not designed (random fibres), strong to be just strong or stiff – other (0-90 fibres), light parameters are also important. And a (sandwich with 0-90 fibre parameter which is typical for naturalfacings) and UD fibre composites is their lower density (unidirectional fibres). compared to glass-fibre composites. Fibre volumes are typical Therefore, it is interesting to look at for the production specific properties. technique, ranging about 20% for the random fibres to about 40% for the As an indication, the properties of unidirectional fibres, aluminium (ρ = 2.7 kg/dm3, E = 72 resulting in a density of GPa, σ = 345 MPa) and steel (carbon, ρ about 1.2-1.3 kg/dm3 for = 7.8 kg/dm3, E = 210 GPa, σ = 770 the natural-fibre MPa) are included in the figure. In this composites and 1.4-1.7 comparison, the properties of naturalkg/dm3 for the glass-fibre fibre composites are more favourable. composites (except for the Especially, their stiffness is interesting light architectures for application in panel design. In both (sandwich), which all interior and exterior applications, have a density of 0.8-0.9 panels often need to have a solid feel kg/dm3). and be lightweight. A design parameter The results of the tensile for these panels is the value of E1/3/ρ. tests are comparable to what could be expected on the basis of Table 1, In this case, the natural fibres perform although the natural fibres better than the glass-fibre composites underperform a bit on both strength for all fibre architectures and better and stiffness. This is probably due to than aluminium and steel. A practical the adhesion between resin and fibre. translation of this parameter is that a Glass fibres have an advantage here panel with the same weight and surface

No66 July - August 2011 / jec composites magazine

43

Feature automotive



JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011

Table of Contents for the Digital Edition of JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011

Cover
Edito
Point of view: Products for thermoplastic reinforcement
Contents
Agenda of Events
COMPANY & BUSINESS
- In Brief
- Aeronautics
APPLICATIONS
- Sports and leisure
- Civil engineering
MARKET
- Glass fibre
- Human Resources
- South America
- Sustainability
FEATURE AUTOMOTIVE
- Vessel
- Prepreg
- Software
- Thermoplastic
- Biocomposites
- High Performance
RESEARCH & DEVELOPMENT
- Process
- Environment
TECHNOLOGY & INNOVATIONS
- CNC
- Multiaxial
- Thermoplastic
- Traceability
Index
In the world
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - Cover
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 2
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - Edito
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - Point of view: Products for thermoplastic reinforcement
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 5
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - Contents
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 7
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - Agenda of Events
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - Ad1
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - Ad2
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - - In Brief
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - - Aeronautics
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 11
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - - Sports and leisure
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 13
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - - Civil engineering
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 15
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - - Glass fibre
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 17
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 18
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - - Human Resources
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - - South America
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 21
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - - Sustainability
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 23
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 24
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 25
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - - Vessel
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 27
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 28
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - - Prepreg
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 30
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 31
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - - Software
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 33
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - - Thermoplastic
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 35
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 36
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 37
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 38
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - - Biocomposites
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 40
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 41
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 42
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 43
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 44
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 45
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - - High Performance
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 47
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - - Process
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 49
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - - Environment
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 51
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 52
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - - CNC
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 54
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 55
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - - Multiaxial
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - - Thermoplastic
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 58
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - - Traceability
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 60
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - Index
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - In the world
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 63
JEC COMPOSITES MAGAZINE - Issue #66 - July/August 2011 - 64
https://www.nxtbook.fr/newpress/jeccomposites/jcm2211_148
https://www.nxtbook.fr/newpress/jeccomposites/jcm2209_147
https://www.nxtbook.fr/newpress/jeccomposites/jcm2206_146
https://www.nxtbook.fr/newpress/jeccomposites/jcm2204_145
https://www.nxtbook.fr/newpress/jeccomposites/jcm2201_144
https://www.nxtbook.fr/newpress/jeccomposites/jcm211_143
https://www.nxtbook.fr/newpress/jeccomposites/jcm2109_142
https://www.nxtbook.fr/newpress/jeccomposites/jcm2107_141
https://www.nxtbook.fr/newpress/jeccomposites/jcm2105_140
https://www.nxtbook.fr/newpress/jeccomposites/jcm2103_139
https://www.nxtbook.fr/newpress/jeccomposites/jcm-experts-digest-additive-manufacturing-2020
https://www.nxtbook.fr/newpress/jeccomposites/jcm2101_138
https://www.nxtbook.fr/newpress/jeccomposites/jcm2011_Special_Issue4
https://www.nxtbook.fr/newpress/jeccomposites/jcm2011_137
https://www.nxtbook.fr/newpress/jeccomposites/jcm2009_136
https://www.nxtbook.fr/newpress/jeccomposites/jcm2007_135
https://www.nxtbook.fr/newpress/jeccomposites/jcm_2020_Q1_Innovation_Report
https://www.nxtbook.fr/newpress/jeccomposites/jcm2005_Special_Issue3
https://www.nxtbook.fr/newpress/jeccomposites/jcm2005_134
https://www.nxtbook.fr/newpress/jeccomposites/jcm2003_133
https://www.nxtbook.fr/newpress/jeccomposites/jcm2001_132
https://www.nxtbook.fr/newpress/jeccomposites/jcm1911_Special_Issue2
https://www.nxtbook.fr/newpress/jeccomposites/jcm1911_131
https://www.nxtbook.fr/newpress/jeccomposites/jcm1909_130
https://www.nxtbook.fr/newpress/jeccomposites/jcm1907_129
https://www.nxtbook.fr/newpress/jeccomposites/jcm1905_128
https://www.nxtbook.fr/newpress/jeccomposites/jcm1903_Special_Issue1
https://www.nxtbook.fr/newpress/jeccomposites/jcm1903_127
https://www.nxtbook.fr/newpress/jeccomposites/jcm1901_126
https://www.nxtbook.fr/newpress/jeccomposites/jcm1811_125
https://www.nxtbook.fr/newpress/jeccomposites/jcm1810_124
https://www.nxtbook.fr/newpress/jeccomposites/jcm1808_123
https://www.nxtbook.fr/newpress/jeccomposites/jcm1807_122
https://www.nxtbook.fr/newpress/jeccomposites/jcm1805_121
https://www.nxtbook.fr/newpress/jeccomposites/jcm1804_120
https://www.nxtbook.fr/newpress/jeccomposites/jcm1803_119
https://www.nxtbook.fr/newpress/jeccomposites/jcm1802_119-Supplement_Innovation_Report
https://www.nxtbook.fr/newpress/jeccomposites/jcm1801_118
https://www.nxtbook.fr/newpress/jeccomposites/jcm1711_117
https://www.nxtbook.fr/newpress/jeccomposites/jcm1710_116
https://www.nxtbook.fr/newpress/jeccomposites/jcm1708_115
https://www.nxtbook.fr/newpress/jeccomposites/jcm1707_114
https://www.nxtbook.fr/newpress/jeccomposites/jcm1706_113
https://www.nxtbook.fr/newpress/jeccomposites/jcm1704_112
https://www.nxtbook.fr/newpress/jeccomposites/jcm1703_111
https://www.nxtbook.fr/newpress/jeccomposites/jcm1701_110
https://www.nxtbook.fr/newpress/jeccomposites/jcm1611_109
https://www.nxtbook.fr/newpress/jeccomposites/jcm1610_108
https://www.nxtbook.fr/newpress/jeccomposites/jcm1608_107
https://www.nxtbook.fr/newpress/jeccomposites/jcm1607_106
https://www.nxtbook.fr/newpress/jeccomposites/jcm1605_105
https://www.nxtbook.fr/newpress/jeccomposites/jcm1604_104
https://www.nxtbook.fr/newpress/jeccomposites/jcm1603_103
https://www.nxtbook.fr/newpress/jeccomposites/jcm1601_102
https://www.nxtbook.fr/newpress/jeccomposites/jcm1511_101
https://www.nxtbook.fr/newpress/jeccomposites/jcm1510_100
https://www.nxtbook.fr/newpress/jeccomposites/jcm1509_99
https://www.nxtbook.fr/newpress/jeccomposites/jcm1507_98
https://www.nxtbook.fr/newpress/jeccomposites/jcm1505_97
https://www.nxtbook.fr/newpress/jeccomposites/jcm1504_96
https://www.nxtbook.com/newpress/jeccomposites/jcm1503_95
https://www.nxtbook.com/newpress/jeccomposites/jcm1501_94
https://www.nxtbook.com/newpress/jeccomposites/jcm1412_93
https://www.nxtbook.com/newpress/jeccomposites/jcm1410_92
https://www.nxtbook.com/newpress/jeccomposites/jcm1409_91
https://www.nxtbook.com/newpress/jeccomposites/jcm1406_90
https://www.nxtbook.com/newpress/jeccomposites/jcm1405_89
https://www.nxtbook.com/newpress/jeccomposites/jcm1404_88
https://www.nxtbook.com/newpress/jeccomposites/jcm1403_87
https://www.nxtbook.com/newpress/jeccomposites/jcm1401_86
https://www.nxtbook.com/newpress/jeccomposites/jcm1311_85
https://www.nxtbook.com/newpress/jeccomposites/jcm1310_84
https://www.nxtbook.com/newpress/jeccomposites/jcm1308_83
https://www.nxtbook.com/newpress/jeccomposites/jcm1307_82
https://www.nxtbook.com/newpress/jeccomposites/jcm1305_81
https://www.nxtbook.com/newpress/jeccomposites/jcm1304_80
https://www.nxtbook.com/newpress/jeccomposites/jcm1303_79
https://www.nxtbook.com/newpress/jeccomposites/jcm1301_78
https://www.nxtbook.com/newpress/jeccomposites/jcm1212_77
https://www.nxtbook.com/newpress/jeccomposites/jcm1210_76
https://www.nxtbook.com/newpress/jeccomposites/jcm1208_75
https://www.nxtbook.com/newpress/jeccomposites/jcm1207_74
https://www.nxtbook.com/newpress/jeccomposites/jcm1206_73
https://www.nxtbook.com/newpress/jeccomposites/jcm1204_72
https://www.nxtbook.com/newpress/jeccomposites/jcm1203_71
https://www.nxtbook.com/newpress/jeccomposites/jcm1201_70
https://www.nxtbook.com/newpress/jeccomposites/jcm1111_69
https://www.nxtbook.com/newpress/jeccomposites/jcm1110_68
https://www.nxtbook.com/newpress/jeccomposites/jcm1108_67
https://www.nxtbook.com/newpress/jeccomposites/jcm1107_66
https://www.nxtbook.com/newpress/jeccomposites/jcm1105_65
https://www.nxtbook.com/newpress/jeccomposites/jcm1104_64
https://www.nxtbook.com/newpress/jeccomposites/jcm1103_63
https://www.nxtbook.com/newpress/jeccomposites/jcm1101_62
https://www.nxtbook.com/newpress/jeccomposites/jcm1011_61
https://www.nxtbook.com/newpress/jeccomposites/jcm1010_60
https://www.nxtbook.com/newpress/jeccomposites/jcm1009_59
https://www.nxtbook.com/newpress/jeccomposites/jcm1006_58
https://www.nxtbook.com/newpress/jeccomposites/jcm1005_57
https://www.nxtbook.com/newpress/jeccomposites/jcm1004_56
https://www.nxtbook.com/newpress/jeccomposites/jcm1003_55
https://www.nxtbook.com/newpress/jeccomposites/jcm1001_54
https://www.nxtbook.com/newpress/jeccomposites/jcm0911_53
https://www.nxtbook.com/newpress/jeccomposites/jcm0910_52
https://www.nxtbook.com/newpress/jeccomposites/jcm0909_51
https://www.nxtbook.com/newpress/jeccomposites/jcm0907-08_50
https://www.nxtbook.com/newpress/jeccomposites/jcm0906_49
https://www.nxtbook.com/newpress/jeccomposites/jcm0904_48
https://www.nxtbook.com/newpress/jeccomposites/jcm0903_47
https://www.nxtbook.com/newpress/jeccomposites/jcm0901_46
https://www.nxtbook.com/newpress/jeccomposites/jcm0811_45
https://www.nxtbook.com/newpress/jeccomposites/jcm0810_44
https://www.nxtbook.com/newpress/jeccomposites/jcm0809_43
https://www.nxtbook.com/newpress/jeccomposites/jcm0807_42
https://www.nxtbook.com/newpress/jeccomposites/jcm0806_41
https://www.nxtbook.com/newpress/jeccomposites/jcm0805_40
https://www.nxtbook.com/newpress/jeccomposites/jcm0803_39
https://www.nxtbook.com/newpress/jeccomposites/jcm0801_38
https://www.nxtbook.com/newpress/jeccomposites/jcm0712_37
https://www.nxtbook.com/newpress/jeccomposites/jcm0710_36
https://www.nxtbook.com/newpress/jeccomposites/jcm0709_35
https://www.nxtbook.com/newpress/jeccomposites/jcm0707_34
https://www.nxtbook.com/newpress/jeccomposites/jcm0706_33
https://www.nxtbookmedia.com